1. Kumaşın büzülme hızı
The shrinkage rate of fabric refers to the percentage of shrinkage of fabric after washing or soaking in water. Generally speaking, the fabrics with the smallest shrinkage rate are synthetic fibers and their blended chemical fiber fabrics, followed by wool fabrics and linen fabrics. Cotton fabrics are in the middle and shrink more, while the largest ones are viscose fibers, Yapay pamuk ve yapay yün kumaşlar .
Sıradan kumaşların büzülme oranı:
Pamuk%4 --10%; kimyasal lif%4 --8%; pamuk polyester 3 .%5 --5.5%; Doğal beyaz kumaş%3'tür; Yün mavi kumaş 3-4%; Poplin 3-4.5%; Çiçek bezi 3-3.5%; Haki Gabardine 4-5.5; Twill%4'tür; Serge 3-4%; Denim%10'dur; Yapay pamuk%10'dur.
2. Kumaş büzülmesine neden olan faktörler:
① Different raw materials of fabrics have different shrinkage rates. Generally speaking, fibers with high hygroscopicity will swell after being soaked in water, their diameter will increase, their length will shorten, and their shrinkage rate will be large. For example, some viscose fibers have a water absorption rate of up to 13%, while synthetic fiber fabrics have poor hygroscopicity and their Büzülme oranı küçüktür .
② Farklı kumaş yoğunlukları farklı büzülme oranlarına sahiptir . Örneğin, çözgü ve atkı talimatlarındaki yoğunluk benzerse, çözgü ve atkı yönlerindeki büzülme oranları, yüksek çözgü yoğunluğuna sahip, daha fazla Weft ile daha fazla darbeye daha fazla daralır ve Fabrics ile Fabrics ile Fabrics, Fabrics ile Fabrics ile Fabrics atkı yönü .
③ Farklı iplik sayısı kumaşların farklı büzülme oranları vardır . Kaba iplik sayımları olan kumaşlar büyük bir büzülme oranına sahiptir, ince iplik sayımları olan kumaşların küçük bir büzülme oranı vardır .
④ Farklı kumaş üretim süreçleri farklı büzülme oranlarına sahiptir . Genel olarak konuşursak, kumaşların dokuma ve boyama işlemi sırasında, liflerin birçok kez gerilmesi gerekir ve işlem süresi .}} daha büyük gerginliğe sahip kumaşlar daha fazla büzülür ve mengene {2}